Single-step process to improve the mechanical properties of carbon nanotube yarn

• Maria Cecilia Evora,
• Xinyi Lu,
• Nitilaksha Hiremath,
• Nam-Goo Kang,
• Kunlun Hong,
• Roberto Uribe,
• Gajanan Bhat and
• Jimmy Mays

Beilstein J. Nanotechnol. 2018, 9, 545–554, doi:10.3762/bjnano.9.52

• ± 68.4 MPa) by more than 75% and the modulus (21.5 ± 0.6 GPa) by more than 144% as compared to untreated CNT yarn (strength 251 ± 26.5 MPa and modulus 8.8 ± 1.2 GPa). Keywords: carbon nanotube yarns; crosslinking; electron beam; grafting; Introduction Due to their exceptional mechanical, thermal, and

• 100 °C for more than 6 h. They found some improvement in mechanical properties of CNT yarn infiltrated with polymers [43]. Hiremath et al. also concluded the same when they investigated the effect of toluene and polystyrene infiltrated in the microstructure of carbon nanotube yarns [44]. The results